Name: 1K101 Transformer Iron Core Material Nanocrystalline Strip And Core 0025mm Thickness
Brand: OHMALLOY
Price: 1 USD

Add to Cart

1K107 Transformer Core Material , Nanocrystalline Strip And Core 0.025mm Thickness

Application area:

l Switch power transformer and Pulse transformer iron core

l EMC common mode inductance and differential mode inductance iron core

Saturable reactor, magnetic amplifier, Spike killer, Pulse Compressor iron core and magnetic bead

Features:

High Saturation magnetic induction - reduce transformer volume
High magnetic permeability low coercive force- improve transformer efficiency, mutual inductor sensitivity, reduce coil distribution parameters
Low loss- reduce transformer temperature rise
Good temperature stability - under 130℃ for long-term work
Lower price - has the best cost performance of all the metal soft magnetic material

Typical Properties

Physical properties of Nanocrystalline alloy

Saturation magnetic induction (Bs)	1.25T	Hardness (Hv)	880
Curie temperature (TC)	560℃	Density (d)	7.2g/cm3
Crystallizing temperature( Tx)	510℃	Resistivity(r)	90mW-cm
Saturation magnetostriction coefficient (ls)	<2×10^-6	Continuous operating temperature range	-55－130℃

Magnetic properties of Nanocrystalline alloy

Product Type	Transverse magnetic annealing	No magnetic annealing	Longitudinal magnetic annealing
Initial permeability	>2×10⁴	>8×10⁴	>1×10⁴
Maximum permeability	>5×10⁴	>45×10⁴	>50×10⁴
Residual magnetic induction	<0.2 T	0.6 T	>0.85 T
Coercive force	<1.8A/m	<0.8A/m	<1.8A/m
Iron loss P(20kHz, 0.5T)	<30W/kg	<50 W/kg	<90W/kg
Iron loss P(100kHz, 0.3T)	<150W/kg	<150 W/kg	<300W/kg
Iron loss rate(-55°C –125C )	<15%	<15%	<15%

The comparison between Nanocrystalline alloy and Permalloy iron alloy

Basic parameter	Superfine crystal iron core	Permalloy iron alloy (1J85)	Ferrite
Saturation magnetic induction Bs(T)	1.25	0.75	0.5
Residual magnetic induction Br(T)	0.2～0.9	-	0.20
Saturation magnetostriction coefficient (×10^-6)	<2	<2	4
Resistivity (mmW-cm )	80	56	10⁶
Curie temperature ∕℃	570	400	<200
Initial permeability μ₀(Gs/Oe)	＞8×10⁴	＞8×10⁴	-
Maximum permeability μ_m(Gs/Oe)	＞50×10⁴	60×10⁴	4×10⁴
Coercive force Hc (A/m)	<2	<1	6
Iron loss (20KHz,0.5T) (W/Kg)	<35	-	No
Iron loss (50KHz,0.3T) (W/Kg)	<50	-	No

Product Tags:

toroidal transformer core material

Inquiry Cart 0

Send your message to this supplier


*From:	Your email address is incorrect!
*To:	Ohmalloy Material Co.,Ltd
*Subject:	Subject is empty!
*Message:	For the best results, we recommend including the following details: -Self introduction -Required specifications -Inquire about price/MOQ Characters Remaining: (0/3000) Please enter 20 to 3000 characters to contact this supplier!

Explore more Transformer Core Material products from this supplier

Find Similar Products By Category:

Minerals & Metallurgy

Hot Searches: